THE INFLUENCE OF STRENGTH MISMATCHING ON THE FRACTURE PROPERTIES OF HETEROGENEOUS JOINTS
DOI:
https://doi.org/10.18690/jet.5.4.27-36.2012Keywords:
strength mismatching, fracture properties, steel jointsAbstract
The differences in mechanical properties among different weld regions affect the strain distribution around the crack tip during fracture toughness tests and consequently influence the fracture toughness values. This paper demonstrates that both strength and toughness affect the fracture behaviour of such complex weldments. High toughness of weld metal is necessary to enable local plastic deformation and to prevent brittle fractures. It is of the utmost importance not to exclude the possibility of plane faults and the appearance local brittle zones in steel welded joints, which can cause failure in heat affected zones and also in weld metal.
Downloads
References
Praunseis, Z.: The influence of Strength Under-matched Weld Metal containing Heterogeneous Regions on Fracture Properties of HSLA Steel Weld Joint (Dissertation in English). Faculty of Mechanical Engineering, University of Maribor, Slovenia, 1998
Praunseis, Z., Toyoda, M., Sundararajan, T.: Fracture behaviours of fracture toughness testing specimens with metallurgical heterogeneity along crack front. Steel res., Sept. 2000, 71, no. 9,
Praunseis, Z., Sundararajan, T., Toyoda, M., Ohata, M.: The influence of soft root on fracture behaviors of high-strength, low-alloyed (HSLA) steel weldments. Mater. manuf. process., 2001, vol. 16, 2
Sundararajan, T., Praunseis, Z.: The effect of nitrogen-ion implantation on the corrosion resistance of titanium in comparison with oxygen- and argon-ion implantations. Mater. technol., 2004, vol. 38, no. 1/2.